Structural Steel FAQ, Part 4 – Evaluating the Presence of Dust

As an expert in the surface finishing industry, Rosler Metal Finishing knows that all the expertise in the world won’t do any good if the surface of the work piece is not properly prepared. When it comes to structural steel, we receive many frequently asked questions about preparation. This installment of our Structural Steel FAQ series will answer How is the presence of dust on shot blasted structural steel components evaluated?

The Dangers of Dust

Blast-cleaned structural steel surfaces must be completely free of dust to ensure proper coating and painting.sgfdfsdfgdf

Residual dust will reduce the adhesion of subsequently applied coatings and, by absorbing moisture, may promote the corrosion of the blast‐cleaned steel surfaces. The potential accumulation of dust is especially critical on horizontal surfaces, the interior of pipes, and in structural cavities.

Special inspections must be carried out to ensure that such areas are adequately cleaned and free from dust before painting.

Continue reading Structural Steel FAQ, Part 4 – Evaluating the Presence of Dust

Structural Steel FAQ, Part 3 – Evaluating Rust and Mill Scale Pre- and Post-Blast

Surface preparation can account for up to 40 percent of structural steel painting and repainting jobs. As Rosler Metal Finishing’s Structural Steel FAQ series has already established, the life of anti‐corrosion coatings on a steel surface depends to a large extent

inside_painting_cabinet1_4004
Application of anti-corrosion paint in a preservation line blasting system.

on how thoroughly this surface has been prepared for painting.

Properly evaluating the surface of structural steel surfaces for coating before and after shot blasting will help balance the cost of preparing, repairing, and monitoring structural steel throughout its impressive lifespan.

This installment of our Structural Steel FAQ series will answer How are rust and mill scale evaluated pre and postblast?

The Standards

Widely used standards were developed to visually assess the initial surface conditions and the quality of the required surface preparation relative to the initial steel surface conditions.

The dominant standards for evaluating rust and mill scale are ISO 8501‐1:2007 (based on the Swedish standard SIS 05 59 00), SSPC Vis 1‐89, and NACE. While different in some minor details, these standards are practically identical.

Continue reading Structural Steel FAQ, Part 3 – Evaluating Rust and Mill Scale Pre- and Post-Blast